1)
Reduce in hazards due to static electricity. (antistatic
film)
2) A
general heat-seal type, non-powder, and metallocene LLDPE.
3) Suitable
for use in laminates and automatic packaging.
4) Offers superior heat-seal
characteristics, impact resistance, and blocking resistance.
[Application]
Granular
matter and the like with an aversion to static electricity.
[Property1]
| Measured item | Units | LL-MTNAS | Measurement method | |
| Thickness | mm | 50 | JIS-K-7130 | |
| Heat bonding temperature |  |
Seal surface | 109 | Futamura Method*1 |
| Blocking strength | N | 0 | Futamura Method*2 | |
| Static prevention | % | Corona surface | 21 | Futamura Method |
| Seal surface | 32 | |||
| Inherent surface resistance |  |
Corona surface | 2*1012 | Futamura Method |
| Seal surface | 5*1012 | |||
*1
)Heat
bonding temperature: 3 N (15-mm width)
*2)
Blocking conditions: 24 hrs, 60,
and 2 kg/4 cm2
Caution: The above properties are a sample measurement and are not standard
values.
Measurement conditions:23
50% RH
[Property2]
| Measured item | Units | Measured surface | LL|MTNAS |
| Static prevention after DL lamination | % | NY surface | 3 |
| LL surface | 24 | ||
| Inherent surface resistance after DL lamination | |
NY surface | More than 1014 |
| LL surface | 6*1012 |
| Dry
laminate conditions: Using
CAT-56 TM-593, an ester adhesive agent from Toyo-Morton Aging conditions : 48 hrs, 40
|
|
| Caution:
The
above properties are a sample measurement and are not standard
values.
Measurement conditions : 23
50% RH
|